- Arts & Culture 6206
- Business & Economics 673
- Computers 316
- Dictionaries & Encyclopedias 71
- Education & Science 76828
- Abstracts 73
- Astrology 4
- Biology 8
- Chemistry 4010
- Coursework 15549
- Culture 8
- Diplomas 316
- Drawings 1596
- Ecology 5
- Economy 76
- English 80
- Ethics, Aesthetics 3
- For Education Students 17562
- Foreign Languages 11
- Geography 3
- Geology 1
- History 88
- Maps & Atlases 5
- Mathematics 12624
- Musical Literature 2
- Pedagogics 19
- Philosophy 22
- Physics 15120
- Political Science 5
- Practical Work 59
- Psychology 63
- Religion 4
- Russian and culture of speech 8
- School Textbooks 7
- Sociology 9
- Summaries, Cribs 87
- Test Answers 160
- Tests 8747
- Textbooks for Colleges and Universities 32
- Theses 7
- To Help Graduate Students 14
- To Help the Entrant 38
- Vetting 382
- Works 13
- Информатика 8
- Engineering 894
- Fiction 706
- House, Family & Entertainment 84
- Law 128
- Website Promotion 68
49. (2) A sample of a standard aluminum alloy containin
Refunds: 0
Uploaded: 25.04.2018
Content: 49-2.rar 31,01 kB
Product description
49. (2) A sample of a standard aluminum alloy containing 12.50% Si, weighing 0.3000 g, was dissolved in a 500.0 ml flask. To construct the calibration curve, 5.00 were placed in volumetric flasks with a capacity of 100.0 ml; 5.20; 5.40; 5.60; 5.80; 6.00 ml of this solution, added reagents - solutions of ammonium molybdate and iron (II) sulphate and brought to the mark. Optical densities relative to the first solution were measured and obtained:
Vst, ml 5.20 5.40 5.60 5.80 6.00
Aotn 0.105 0.215 0.330 0.440 0.550
A sample of the analyzed alloy weighing 0.2500 g was dissolved in a flask with a capacity of 500.0 ml. A sample of 5.00 ml was placed in a 100.0 ml volumetric flask, reagents were added and the relative density was measured, as in the construction of the calibration curve.
Calculate the mass fraction (%) of silicon in the samples according to the following data:
2) Aot.x = 0.360
Additional information
If you do not open the file - install the RAR archiver. Inside the archive you will find a solution in Word format.Problems in optics and from the collection of problems and problems in analytical chemistry, ed. Vasilyeva V.P.
Feedback
0| Period | |||
| 1 month | 3 months | 12 months | |
| 0 | 0 | 0 | |
| 0 | 0 | 0 | |